Ti 6al 4v titanium pipe / Grade 5 titanium tube are typically manufactured according to various industry standards, such as ASTM B338 and AMS 4943. These standards define the chemical composition, mechanical properties, and testing requirements for titanium tubes.
Titanium Pipe Characteristics
| Особеност | Typical Value / Description | Common Applications |
|---|---|---|
| Материал | Ti-6Al-4V (Titanium Grade 5) | Aerospace (hydraulic lines, structural tubes) |
| Key Properties | High strength-to-weight ratio, excellent corrosion resistance, good weldability | Chemical Processing (heat exchangers, pressure piping) |
| Common Standards | ASTM B861, ASTM B338, ASME SB861 | Medical (surgical implants) |
| Manufacturing | Seamless (hot finished / cold drawn) | Marine & Offshore (seawater piping, desalination) |
| Сила | Tensile Strength: ≥ 895 MPa | Power Generation, Oil & Gas |
What is Ti-6Al-4V (Grade 5) Titanium Alloy?
Ti-6Al-4V, also known as Grade 5 Титан, is the most widely used titanium alloy globally, often called the “workhorse” of the titanium industry. Its name comes from its chemical composition: 6% Aluminum and 4% Vanadium, with the balance being Titanium .
Ti-6Al-4V Titanium pipes are manufactured without a welded seam, providing superior strength and reliability for critical applications. They are typically produced to international standards such as ASTM B861 (general seamless pipes) and ASTM B338 (heat exchanger tubes)
Ti-6Al-4V Grade 5 titanium pipe provide an unmatched combination of lightweight durability and corrosion resistance. Whether for aerospace, medical, or industrial applications, they are the premium choice for engineers demanding the highest level of performance
The chemical composition of Grade 5 or 6al 4v titanium seamless pipes are as follows:
– Titanium: 88.6%
– Aluminum: 6.0%
– Vanadium: 4.0%
– Iron: 0.25%
– Oxygen: 0.20%
– Carbon: 0.08%
– Nitrogen: 0.05%
The mechanical properties of 6al 4v titanium pipes are as follows:
– Tensile strength: 110 ksi (758 MPa)
– Yield strength: 100 ksi (689 MPa)
– Elongation: 10%
– Hardness: 36 HRC
| Allowable deviation of outer diameter of titanium pipe（mm） | ||||||
| Навън | 3-10 | >10-30 | >30-50 | >50-80 | >80-100 | >100 |
| allowable variation | ±0.15 | ±0.30 | ±0,50 | ±0.65 | ±0.75 | ±0.85 |
Titanium Pipes can be supplied with various finishes, including pickled, polished, bright annealed, or sandblasted, depending on the application
| Length of Titanium pipe（mm） | ||||
| Titanium seamless tube | outside | ≤15 | Indefinite дължина | 500-400 |
| 15 | 500-900 | |||
| Titanium welded pipe | thickness | 0.5-1.25 | 500-1500 | |
| 1.25-2.0 | 500-6000 | |||
| Titanium welded – rolled tube | thickness | 2.0-2.5 | 500-4000 | |
| 0.5-0.8 | 500-8000 | |||
| >0.8-20 | 500-5000 | |||